PC K10 is a high heat-resistance PC material for industrial FDM/FFF 3D printers. With mechanical properties comparable to normal PC materials, its softening temperature is increased by more than 30°C, which is close to PEI, but easier to print than PEI.
Basic Physical Properties:
| PC K10 | Printed copy (horizontal printing of sample, 100% linear filling) | Injection molded parts | Test standards |
| Density (g/cm3) | 1.18-1.20 | ISO 1183 | |
| Melt flow rate (MFR) 1 | 30-35 | ISO 1133 | |
| Heat deflection temperature(HDT)2 | 163 | ISO 75 | |
| Vicat softening temperature(VST)3 | 176 | ISO 306 | |
| Tensile strength (MPa) | 65-70 | ISO 527 | |
| Elongation at break(%) | 8-12 | ||
| Maximum force(Mpa) | 97-105 | ISO 178 | |
| Flexural modulus(Mpa) | 2300-2600 | ||
| Impact strength(KJ/m2) | 43-47 | ISO 179 | |
| Notch impact strength1(KJ/m2) | 3-6 | ||
*1. Test condition: temperature (T)=330 ℃; Mass (m)=2.16kg.
*2. Test condition: bending stress=0.45MPa; Heating rate=120 ℃/h.
*3. Test condition: load=10N; Heating rate=120 ℃/h.